| CCS | Bulk Density | Porosity | Temperature | Applications |
| 1.5≥MPa | 0.70-0.85 g/cm3 | 80-87% | 1700≤ ℃ | Steel |
Silicon Carbide Ceramic Foam Filters
| CCS | Bulk Density | Porosity | Temperature | Pore Size (PPI) | Applications |
| 1.5≥MPa | 0.40-0.55 g/cm3 | 80-87% | 1500≤ ℃ | 10-15-20 | Ductile Iron, Gray Iron, Bronze |
Alumina Ceramic Foam Filters
| Compressive Str. | Bulk Density | Porosity | Temperature | Pore Size (PPI) | |
| 1.2≥MPa | 0.36-0.45 g/cm3 | 80-90% | 1150≤ ℃ | Casting | 10-25 |
| Semi-Continuous | 30-60 | ||||
| HQ Aluminum | 50-60 | ||||
| Continuous Casting and Rolling | 50-60 | ||||
Mesh Filters
| Type | Steel Casting | Iron Casting | Aluminum Casting |
| Application Temp. | 1600-1650⁰C | 1400-1450⁰C | 850⁰C |
| Softening Temp. | 1750⁰C | 1750⁰C | 1200⁰C |
| Continuous App. | <15 sec. | <10 sec. | <10 sec. |
| Tensile Str. | >16kg/4 | >8kg/4 | >6kg/4 |
| Gas Emission | <60cm3/g | <60cm3/g | <30cm3/g |
| Density | 580g/m3 | 195g/m3 | 300g/m3 |
| Hole Size | 1.5x1.5mm / 2.0x2.0 / 2.5x2.5mm | 1.5x1.5mm / 2.0x2.0 / 2.5x2.5mm | 1.5x1.5mm / 2.0x2.0 / 2.5x2.5mm |
| Weave Pattern | Leno, Mock-Leno | Leno, Mock-Leno | Leno, Mock-Leno |
| Open Area | 50-60% | 50-60% | 50-60% |
Ceramic Filters