No-bake Furan Resin
Suitable for production of steel, iron, nonferrous castings, with excellent quality records. Sand core (mold) is easy collapsible, reclaimable, and reduces the consumption of original sand.
Suitable for production of steel, iron, nonferrous castings, with excellent quality records. Sand core (mold) is easy collapsible, reclaimable, and reduces the consumption of original sand.
| Model | Density (20℃) g/cm3 |
Viscosity (20℃) ≤mPa.S |
Formaldehyde Free | Nitrogen | Shelf Life | Application Range |
| 7501 | 1.20-1.30 | 400 | ≤0.5% | ≤7% | 6 months | non-ferrous |
| 86-A | 1.12～1.18 | 40 | ≤0.3% | ≤3% | 6 months | grey, ductile iron |
| 85-2 | 1.12～1.20 | 40 | ≤0.3% | ≤2% | 6 months | various iron |
| 85-4 | 1.10～1.20 | 40 | ≤0.3% | ≤4% | 6 months | various iron |
| 90-0 | 1.10～1.20 | 30 | ≤0.3% | ≤0.3% | 6 months | big steel and alloys |
| 90-1 | 1.10～1.18 | 30 | ≤0.3% | ≤1% | 6 months | steel, big ductile |
| 90-2 | 1.10～1.18 | 30 | ≤0.3% | ≤2% | 6 months | various iron |
| 95-l | 1.12～1.18 | 30 | ≤0.3% | ≤1.5% | 6 months | big steel and alloys |
No-bake Phenolic Urethane Resin
Sand core/mold has good collapsibility and easy to reclaim. It can reduce the crack defects and the consumption of original sand. Suitable for steel, iron, nonferrous castings, and it has excellent quality records for these castings; free of sulfur and phosphorus.
| Model | Phenolic Resin ID-1610/1620 |
Polyisocyanate ID-2610/2620 |
| Appearance | light yellow to brown | brown liquid |
| Density(25℃)g/cm3 | 1.05～1.15 | 1.00～1.15 |
| Viscosity(25℃) mpa.s | ≤250 | ≤100 |
| Shelf Life (month) | 6 | 6 |
Ester Cured Alkaline Phenolic Resin
This binder system doesn’t contain harmful foundry elements: Nitrogen, sulfur, phosphorus, etc. , especially suitable for the production of steel alloys, carbon steel, ductile iron casting.
| Model | Appearance | Density (20℃) g/cm3 |
Viscosity (25℃) mPa·s |
Free Formaldehyde | Ph Value | Shelf Life (≤25℃) |
| ID-201 | brown red | 1.25±0.05 | ≤150 | ≤0.1% | ≥12 | 3 months |
| ID-201D | brown red | l.25±0.05 | ≤90 | ≤0.1% | ≥12 | 3 months |
CO2 Cured Alkaline Phenolic Resin
Free of N. P. S. etc harmful elements, especially suitable for the production of steel alloys, carbon steel and ductile iron castings, keep off foundry defects caused by N. P. S.
Free of N. P. S. etc harmful elements, especially suitable for the production of steel alloys, carbon steel and ductile iron castings, keep off foundry defects caused by N. P. S.
| Model | Appearance | Density (20℃) g/cm3 |
Viscosity (25℃) mPa·s |
Free Formaldehyde | Shelf Life (≤25℃) |
| ID-680 | red / brown | 1.30±0.05 | ≤300 | ≤0.1% | 6 months |
Easy-collapsible Urethane No-bake Resin Special for Aluminum Casting
Excellent fluidity of the mixture, easy for manual or mechanical sand filling, good roughness of casting surface and high dimensional accuracy.
| Model | Phenolic Resin ID-1610/1620 |
Polyisocyanate ID-2610/2620 |
| Appearance | light yellow to brown | brown liquid |
| Density(25℃)g/cm3 | 0.85～1.15 | 1.00～1.15 |
| Viscosity(25℃) mpa.s | ≤100 | ≤100 |
Cold Box Resin
Less resin addition rate, lower technical control, less consumption of mould releasing agent and cleaning agent, lower shooting pressure, higher strength, less cleanups, higher utilization, lower rejection rate, better working circumstance, more environment friendly.
Less resin addition rate, lower technical control, less consumption of mould releasing agent and cleaning agent, lower shooting pressure, higher strength, less cleanups, higher utilization, lower rejection rate, better working circumstance, more environment friendly.
| Type | Phenolic Resin | Polyisocyanate |
| Model | XLI-318M, XLI-395 | XLII-618, XLII-695 |
| Appearance | light yellow to brown | brown |
| Density(20℃)g/cm3 | 1.05-1.15 | 1.05-1.20 |
| Viscosity(25℃)mpa.s | ≤250 | ≤100 |
Resin Series